Refractoriness (℃): | 1580< Refractoriness< 1770 |
---|---|
Feature: | Long Time Materials |
Type: | Refractory Material |
Shape: | Brick |
Material: | Magnesia-Hecynite |
Application Area: | Sintering Zone in Rotary Kiln |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Chemical Composition | UNIT | Working layer | Insulation layer |
MgO | % | 85-87 | 67 |
Al2O3 | % | 9-11 | 1.8 |
SiO2 | % | 0.65 | / |
Fe2O3 | % | 0.6 | / |
CaO | % | 1.4 | / |
Physical Properties | UNIT | Working layer | Insulation layer |
Bulk Density | g/cm3 | 2.9-3.0 | 2.6 |
Apparent Porosity | % | 17 | 24 |
Thermal Shock Resistance - in air at 950 °C | cycle | ≥100 | / |
Refractoriness Under Load | °C | 1700 | 1600 |
Thermal Expansion - at 1000 °C | % | 1.26 | 1.1 |
Cold Crushing Strength | MPa | 60 | 30 |
Modulus of Rupture-at1400ºC 0.5h | Mpa | 1.45 | 1.21 |
Thermal Conductivity - at 300 °C | W/mK | 4.0 | 2.508 |
Note: The above datas are the representative average value measured in accordance with the test methods for general purpose and vary with the fluctuations of normal production conditions.These datas are provided as a technical service,sometimes may be adjusted, so they should not be regarded as the product index. |